ULMA FORTIS POWDERED

Type
  • Powdered, Sterile
Material
  • Natural High Grade Rubber Latex
Colour
  • Natural
Design & Features
  • Powdered
    Hand specific, curved fingers, palm textured, beaded cuff.
Storage
  • The gloves shall maintain their properties when stored in a dry condition. Avoid direct sunlight
Shelf-life
  • 5 years from the date of manufacturing

Download BrochureSend Enquiry

 


Functional Benefits:

  • Its excellent fit and reduced finger fatigue and allows long hours of comfortable use.
  • Use of medical grade absorbable dusting powder that ensure the efficient donning each time without fail.
  • This glove is specially formulated for comfort and reduced finger fatigue.
  • This softness and elasticity ensures sensitivity and dexterity for the user’s hands.
  • The curved finger and wide palm fit reduces finger fatigue and allows for long hours of comfortable use.

Quality Standards:

  • Conforms to ASTM D3577, EN455 and ISO 10282 Standards.
  • Manufactured under ISO 13485:2016 Quality Management System.

Glove Sizes:

  • 5.5, 6.0, 6.5, 7.0, 7.5, 8.0, 8.5, 9.0
  • Size of gloves shall be marked in the check box on the shipping carton with black ink
 
Dimension Standard
Top Glove ASTM D3577 EN455 ISO 10282
Glove Length (mm)
5.5
6.0
6.5
7.0
7.5
8.0
8.5
9.0
Min 280
Min 245
Min 265
Min 265
Min 265
Min 265
Min 265
Min 265
Min 265

Min 250
Min 260
Min 260
Min 270
Min 270
Min 270
Min 280
Min 280

Min 250
Min 260
Min 260
Min 270
Min 270
Min 270
Min 280
Min 280
Palm Width (mm)
5.5
6.0
6.5
7.0
7.5
8.0
8.5
9.0

72 ± 4
77 ± 5
83 ± 5
89 ± 5
95 ± 5
102 ± 6
108 ± 6
114 ± 6

70 ± 6
76 ± 6
83 ± 6
89 ± 6
95 ± 6
102 ± 6
108 ± 6
114 ± 6

72 ± 4
77 ± 5
83 ± 5
89 ± 5
95 ± 5
102 ± 6
108 ± 6
114 ± 6

72 ± 4
77 ± 5
83 ± 5
89 ± 5
95 ± 5
102 ± 6
108 ± 6
114 ± 6
Thickness Single Wall (mm)
5.5
6.0
6.5
7.0
7.5
8.0
8.5
9.0
Finger: 0.20±0.02
Palm: 0.18±0.02
Cuff: 0.16±0.02
Finger: Min 0.10
Palm: Min 0.10
Cuff: Min 0.10
N/A Smooth: Min 0.10
Textured: Min 0.13
Property ASTM D3577 EN 455 ISO 10282
Elongation at Break (%)
Before Aging
After Aging

Min 750
Min 560

N/A
N/A

Min 700
Min 550
Tensile Strength (MPa)
Before Aging
After Aging

Min 24
Min 18

N/A
N/A

N/A
N/A
Force at Break (N)
Before Aging
After Aging

N/A
N/A

Med. ≥ 9
Med. ≥ 9

Min 12.5
Min 9.5