STERILE POLYISOPRENE SURGICAL GLOVE

Type
  • Polyisoprene Surgical Glove, Powder Free, Polymer Coated, Sterile
Material
  • Synthetic Polyisoprene latex
Design & Features
  • Hand specific, curved finger, palm textured, beaded cuff
Sterilization
  • Gamma Ray or Electron Beam
Storage
  • The gloves shall maintain their properties when stored in a dry condition. Avoid direct sunlight
Shelf-life
  • 5 years from the date of manufacturing

Download BrochureSend Enquiry

 


Functional Benefits:

  • Provide an alternative solution for individual who are allergic to Natural Rubber Latex
  • Ultralow modulus for greater softness, comfort and fit

Quality Standards:

  • Conforms to ASTM D3577, EN455 and ISO 10282:2014
  • Manufactured under ISO 13485:2016 Quality Management System

Glove Sizes:

  • 5.5, 6.0, 6.5, 7.0, 7.5, 8.0, 8.5, 9.0
  • Size of gloves shall be marked on the shipping carton with black ink

International Quality System Certificate Awarded:



Dimension Standard
Top Glove ASTM D3577 EN455 ISO 10282
Length (mm) Min 280
Min 245 (5.5)
Min 265 (6.0 to 9.0)
Min 250 (5.5)
Min 260 (6.0 to 6.5)
Min 270 (7.0 to 8.0)
Min 280 (8.5 to 9.0)
Min 250 (5.5)
Min 260 (6.0 to 6.5)
Min 270 (7.0 to 8.0)
Min 280 (8.5 to 9.0)
Width (mm)
5.5
6.0
6.5
7.0
7.5
8.0
8.5
9.0

72 ± 4
77 ± 5
83 ± 5
89 ± 5
95 ± 5
102 ± 6
108 ± 6
114 ± 6

70 ± 6
76 ± 6
83 ± 6
89 ± 6
95 ± 6
102 ± 6
108 ± 6
114 ± 6

72 ± 4
77 ± 5
83 ± 5
89 ± 5
95 ± 5
102 ± 6
108 ± 6
114 ± 6

72 ± 4
77 ± 5
83 ± 5
89 ± 5
95 ± 5
102 ± 6
108 ± 6
114 ± 6
Thickness : Single Wall (mm)
Finger
Palm
Cuff

0.22 ± 0.02
0.19 ± 0.02
0.17 ± 0.02

Min 0.10
Min 0.10
Min 0.10


N/A


Smooth area: Min 0.10
Textured area: Min 0.13

Property ASTM D3577 EN455 ISO 10282
Tensile Strength (MPa)
Before Aging
After Aging

Min 17
Min 12

N/A

N/A
Elongation at Break (%)
Before Aging
After Aging

Min 650
Min 490

N/A

Min 600
Min 500
Median Force at Break (N)
Before Aging
After Aging

N/A

Min 9
Min 9

Min 9
Min 9
Force at 300% Elongation (N)
Before Aging
After Aging

N/A

N/A

Max 3
N/A