Maxitex Ortho PF

Type
  • Powder Free, Sterile
Material
  • Natural High Grade Rubber Latex
Colour
  • Brown
Design & Features
  • Hand specific, curved fingers, palm textured, beaded cuff
Storage
  • The gloves shall maintain their properties when stored in a dry condition. Avoid direct sunlight
Shelf-life
  • 5 years from the date of manufacturing

Download BrochureSend Enquiry

 


Functional Benefits:

  • Designed for Prick Risk and Safety: allow better resistance against cut and pricks
  • Enhanced Multi-Layered Polymer Coating: enable users to experience an incredibly smooth donning experience
  • Tough on the outside. Gentle on the inside.
  • This is alternatives to Maxitex Duplex for surgeon whom prefer to wear single gloves. Thicker than normal single gloves to give better protection

Quality Standards:

  • Conforms to ASTM D3577 and EN455 Standards
  • Manufactured under ISO 13485:2016 Quality Management System

GLOVE SIZES:

  • 5.5, 6.0, 6.5, 7.0, 7.5, 8.0, 8.5, 9.0
  • Size of gloves shall be marked in the check box on the shipping carton with black ink
 
Dimension Standard
Top Glove ASTM D3577 EN455 ISO 10282
Glove Length (mm)
5.5
6.0
6.5
7.0
7.5
8.0
8.5
9.0
Min 290
Min 245
Min 265
Min 265
Min 265
Min 265
Min 265
Min 265
Min 265

Min 250
Min 260
Min 260
Min 270
Min 270
Min 270
Min 280
Min 280

Min 250
Min 260
Min 260
Min 270
Min 270
Min 270
Min 280
Min 280
Palm Width (mm)
5.5
6.0
6.5
7.0
7.5
8.0
8.5
9.0

72 ± 4
77 ± 5
83 ± 5
89 ± 5
95 ± 5
102 ± 6
108 ± 6
114 ± 6

70 ± 6
76 ± 6
83 ± 6
89 ± 6
95 ± 6
102 ± 6
108 ± 6
114 ± 6

72 ± 4
77 ± 5
83 ± 5
89 ± 5
95 ± 5
102 ± 6
108 ± 6
114 ± 6

72 ± 4
77 ± 5
83 ± 5
89 ± 5
95 ± 5
102 ± 6
108 ± 6
114 ± 6
Thickness Single Wall (mm)
5.5
6.0
6.5
7.0
7.5
8.0
8.5
9.0
Finger: 0.31±0.02
Palm: 0.30±0.02
Cuff: 0.22±0.02
Finger: 0.10
Palm: 0.10
Cuff: 0.10
N/A Smooth: Min 0.10
Textured: Min 0.13
Property ASTM D3577 EN 455
Elongation at Break (%)
Before Aging
After Aging

Min 750
Min 560

N/A
N/A
Tensile Strength (MPa)
Before Aging
After Aging

Min 24
Min 18

N/A
N/A
Median Force at Break (N)
Before Aging
After Aging

N/A
N/A

Min 9
Min 9