MAXITEX DUPLEX PF

Type
  • Powder free, sterile
Material
  • Natural High Grade Rubber Latex
Colour
  • Inner Glove: Green
  • Outer Glove: Brown
Design & Features
  • Hand specific, Curved fingers, Palm Textured, Beaded Cuff
Storage Condition
  • The gloves shall maintain their properties when stored in a dry condition. Avoid direct sunlight
Shelf-life
  • 5 years from the date of manufacturing

Download BrochureSend Enquiry

 


Functional Benefits:

  • Design for prick and safety: Considerable reduce risks of contact with body fluids due to double glove.
  • Anatomical design curved fingers follow the natural finger shapes at rest to reduce fatique and finger dexterity, even during rigurous procedures.
  • Enhanced multilayered polymer coating enables user to experience and incredibly smooth donning experience

Quality Standards:

  • Conforms to ASTM D3577 , EN 455 , and ISO 10282 Standards
  • Manufactured under ISO 13485:2016 Quality Management System

Glove Sizes:

  • 5.5, 6.0, 6.5, 7.0, 7.5, 8.0, 8.5, 9.0
  • Size of gloves shall be marked in the check box on the shipping carton with black ink
 

Primary Glove

Dimension Standard
Top Glove ASTM D3577 EN455 ISO 10282
Inner Glove Outer Glove
Glove Length (mm)
5.5
6.0
6.5
7.0
7.5
8.0
8.5
9.0
Min 275 Min 295
Min 245
Min 265
Min 265
Min 265
Min 265
Min 265
Min 265
Min 265

Min 250
Min 260
Min 260
Min 270
Min 270
Min 270
Min 280
Min 280

Min 250
Min 260
Min 260
Min 270
Min 270
Min 270
Min 280
Min 280
Palm Width (mm)
5.5
6.0
6.5
7.0
7.5
8.0
8.5
9.0

72 ± 4
77 ± 5
83 ± 5
89 ± 5
95 ± 5
102 ± 6
108 ± 6
114 ± 6

70 ± 6
76 ± 6
83 ± 6
89 ± 6
95 ± 6
102 ± 6
108 ± 6
114 ± 6

72 ± 4
77 ± 5
83 ± 5
89 ± 5
95 ± 5
102 ± 6
108 ± 6
114 ± 6

72 ± 4
77 ± 5
83 ± 5
89 ± 5
95 ± 5
102 ± 6
108 ± 6
114 ± 6
Thickness Single Wall (mm)
5.5
6.0
6.5
7.0
7.5
8.0
8.5
9.0
Finger: 0.18±0.02
Palm: 0.17±0.02
Cuff: 0.16±0.02
Finger: 0.25±0.02
Palm: 0.23±0.02
Cuff: 0.19±0.02
Finger: Min 0.10
Palm: Min 0.10
Cuff: Min 0.10
N/A Smooth: Min 0.10
Textured: Min 0.13
Property ASTM D3577 EN 455 ISO 10282
Elongation at Break (%)
Before Aging
After Aging

Min 750
Min 560

N/A
N/A

Min 700
Min 550
Tensile Strength (MPa)
Before Aging
After Aging

Min 24
Min 18

N/A
N/A

N/A
N/A
Force at Break (N)
Before Aging
After Aging

N/A
N/A

Med. ≥ 9
Med. ≥ 9

Min 12.5
Min 9.5