FUSIONE POWDER FREE

Type
  • Powder Free, Sterile
Material
  • Synthetic Polychloroprene & Polyisoprene Quality Latex
Colour
  • Natural
Design & Features
  • Hand specific, curved fingers, palm textured, beaded cuff
Storage Condition
  • The gloves shall maintain their properties when stored in a dry condition. Avoid direct sunlight
Shelf-life
  • 5 years from the date of manufacturing

Download BrochureSend Enquiry

 


Functional Benefits:

  • Fusione is the top performing synthetic surgical gloves with soft and supple comfort beyond synthetic. Fusione is a result of engineering design and unique material formulation. The gloves exceed the features of any synthetic gloves and yet improves on safety.
  • Fusione is a multilayered technology for safety and comfort because it enhanced and presents an incredible donning experience for the user, even during double donning.
  • Fusione has a micromised peak surface because it enhanced slip-resistance for extra grip and control during surgical procedures.
  • Fusione has a n anatomical design to reduce fatigue and finger dexterity, even during rigorous procedures.
  • The special ergonomically designed mould produce glove of high comfort. The multilayered coating enable excellent double donning damp hand donning with moisture absorbent.

Quality Standards:

  • Conforms to ASTM D3577, EN455 Standards and ISO 10282
  • Manufactured under ISO 13485:2016 Quality Management System

Glove Sizes:

  • 5.5, 6.0, 6.5, 7.0, 7.5, 8.0, 8.5, 9.0
  • Size of gloves shall be marked in the check box on the shipping carton with black ink
 
Dimension Standard
Top Glove ASTM D3577 EN455 ISO 10282
Glove Length (mm)
5.5
6.0
6.5
7.0
7.5
8.0
8.5
9.0
Min 295
Min 245
Min 265
Min 265
Min 265
Min 265
Min 265
Min 265
Min 265

Min 250
Min 260
Min 260
Min 270
Min 270
Min 270
Min 280
Min 280

Min 250
Min 260
Min 260
Min 270
Min 270
Min 270
Min 280
Min 280
Palm Width (mm)
5.5
6.0
6.5
7.0
7.5
8.0
8.5
9.0

72 ± 4
77 ± 5
83 ± 5
89 ± 5
95 ± 5
102 ± 6
108 ± 6
114 ± 6

70 ± 6
76 ± 6
83 ± 6
89 ± 6
95 ± 6
102 ± 6
108 ± 6
114 ± 6

72 ± 4
77 ± 5
83 ± 5
89 ± 5
95 ± 5
102 ± 6
108 ± 6
114 ± 6

72 ± 4
77 ± 5
83 ± 5
89 ± 5
95 ± 5
102 ± 6
108 ± 6
114 ± 6
Thickness Single Wall (mm)
5.5
6.0
6.5
7.0
7.5
8.0
8.5
9.0
Finger: 0.22±0.02
Palm: 0.19±0.02
Cuff: 0.17±0.02
Finger: Min 0.10
Palm: Min 0.10
Cuff: Min 0.10
N/A Smooth: Min 0.10
Textured: Min 0.13
Property ASTM D3577 EN 455 ISO 10282
Elongation at Break (%)
Before Aging
After Aging

Min 650
Min 490

N/A
N/A

Min 600
Min 500
Tensile Strength (MPa)
Before Aging
After Aging

Min 17
Min 12

N/A
N/A

N/A
N/A
Force at Break (N)
Before Aging
After Aging

N/A
N/A

Med. ≥ 9
Med. ≥ 9

Min 9.0
Min 9.0